技术数据

数据概览

收缩	<.001 in. / in.
混合粘度	9,300 cps
断裂伸长率	>1000 %
固化时间	2 hours
颜色	半透明
邵氏硬度	000-35
操作时间	15 minutes
比容	28 cu. in./lb.
比重	0.98 g/cc
体积混合比	1A:1B
重量混合比	1A:1B

Ecoflex™ GEL

Ecoflex ™GEL为极其柔软的铂金固化硅胶凝胶，专为制作硅胶化妆用具、缓冲、制造垫圈，封装和其他需要非常柔软硅胶材料应用场合设计。

经过认证皮肤安全 -固化的Ecoflex™GEL皮肤安全，独立实验室按OECDTG 439认证。

特征

Ecoflex™GEL 的邵氏硬度为000-35，低于邵氏00硬度标准。因为Ecoflex™GE非常柔软，所以它可以很好地用作填充封装硅胶化妆用具和假肢。通过添加Silc Pig™硅胶颜料可以实现无限的色彩效果。

由于Ecoflex GEL在固化时非常粘稠，在某些情况下，建议将Ecoflex™ GEL用一种非粘性铂金固化硅胶（如Dragon Skin FX Pro或其他合适的膜）封装。Ecoflex™ GEL按重量或体积比1A：1B混合。硅胶在室温（73°F / 23°C）下固化，收缩率可忽略不计。

相册

说明

Preparation - Materials should be stored in and used at room temperature (73°F / 23°C). These products have a limited shelf life and should be used as soon as possible. Rubber may be inhibited by sulfur based clays resulting in tackiness at the surface interface or a total lack of cure throughout the mold.

If compatibility between the rubber and the surface is a concern, a small-scale test is recommended. Apply a small amount of rubber onto a non-critical area. Inhibition has occurred if the rubber is gummy or uncured after the recommended cure time has passed.

USING ECOFLEX™ GEL FOR MAKING SILICONE PROSTHETIC MAKEUP APPLIANCES - Ecoflex™ GEL can be used as a gel filler for creating silicone prosthetic appliances. In most cases, Ecoflex™ GEL should be encapsulated. For example, Dragon Skin™ FX-Pro can be stippled onto a mold surface (e.g. Shell Shock™ released with Ease Release™ 200) to create a membrane. Ecoflex™ GEL can then be poured or injected into the mold to create a soft gel prosthetic encapsulated with strong, non-tacky Dragon Skin™ FX-Pro silicone.

Applying a Release Agent - Although not always necessary, a release agent will make demolding easier when casting into most surfaces. Ease Release™ 200 available from Smooth-On is a proven release agent for releasing silicone from silicone or other surfaces.

Because no two applications are quite the same, a small test application to determine suitability for your project is recommended if performance of this material is in question.

MEASURING & MIXING - Before you begin, pre-mix Part B thoroughly. After dispensing required amounts of Parts A and B into mixing container (1A:1B by volume or weight), mix thoroughly making sure that you scrape the sides and bottom of the mixing container several times. For best results, ‘double mix’ the material by pouring the mixture into a new container, then continuing to mix until material is thoroughly blended.

Pouring - For best results, pour your mixture in a single spot at the lowest point of the containment field or mold. Let the rubber seek its own level. A uniform flow will help minimize entrapped air.

Curing - Allow rubber to cure for 2 hours at room temperature (73°F/23°C) before demolding. Time to demold can be reduced with mild heat or by adding an appropriate amount of Plat-Cat™ cure accelerator. The pot life and cure times can be extended using Slo-Jo™ cure retarder. Do not cure rubber where temperature is less than 65°F/18°C.